Wrought iron

Various examples of wrought iron

Steels
Phases
Ferrite Austenite Cementite Martensite Graphite
Microstructures
Spheroidite Pearlite Bainite Ledeburite Tempered martensite Widmanstätten structures
Classes
Crucible steel Carbon steel Spring steel Alloy steel Maraging steel Stainless steel High-speed steel Weathering steel Tool steel
Other iron-based materials
Cast iron Gray iron White iron Ductile iron Malleable iron Wrought iron

Wrought iron is an iron alloy with a very low carbon content (less than 0.05%) in contrast to that of cast iron (2.1% to 4.5%), or 0.25 for low carbon "mild" steel. Wrought iron is manufactured by heating and melting high carbon cast iron in an open charcoal or coke hearth or furnace in a process known as puddling. The high temperatures cause the excess carbon to oxidise, the iron being stirred or puddled during the process in order to achieve this. As the carbon content reduces, the melting point of the iron increases, ultimately to a level which is higher than can be achieved by the hearth, hence the wrought iron is never fully molten and many impurities remain.

The reason for converting high carbon cast iron into low carbon Wrought iron is that although cast iron has very good compressive strength, it is very brittle and at ambient temperatures cannot be bent or shaped without breaking. By contrast Wrought iron is very malleable and strong in bending and tension.

Wrought iron is a semi-fused mass of iron with fibrous slag inclusions (up to 2% by weight), which give it a wood-like "grain" that is visible when it is etched, rusted, or bent to failure. Wrought iron is tough, malleable, ductile, corrosion resistant, and easily forge welded, but is more difficult to weld electrically.

Before the development of effective methods of steelmaking and the availability of large quantities of steel, wrought iron was the most common form of malleable iron. It was given the name wrought because it was hammered, rolled, or otherwise worked while hot enough to expel molten slag. The modern functional equivalent of wrought iron is mild steel, also called low-carbon steel. Neither wrought iron nor mild steel contain enough carbon to be hardened by heating and quenching.^{[1]: 145 [failed verification]}

Due the inherent variability in its relatively crude and labour intensive manufacturing process, also the type of iron used, the properties of wrought iron vary but are generally relatively pure iron with a very low carbon content plus a small amount of mostly silicate slag which forms fibreous or laminar inclusions caused by the hot rolling process used to form it into long bars or rods. Because these silicate inclusions separate layers of iron and form planes of weakness, wrought iron is anisotropic, its strength varying depending on its orientation. Wrought iron may typically be composed of around 99.4% iron by mass.^[2] The presence of slag can be beneficial for blacksmithing operations, such as forge welding, since the silicate inclusions act as a flux and give the material its unique, fibrous structure.^[3] The silicate filaments in the slag also protect the iron from corrosion and may diminish the effect of fatigue caused by shock and vibration.^[4]

Historically, a modest amount of wrought iron was refined into steel, which was used mainly to produce swords, cutlery, chisels, axes, and other edged tools, as well as springs and files. The demand for wrought iron reached its peak in the 1860s, being in high demand for ironclad warships and railway use. However, as properties such as brittleness of mild steel improved with better ferrous metallurgy and as steel became less costly to make thanks to the Bessemer process and the Siemens–Martin process, the use of wrought iron declined.

Many items, before they came to be made of mild steel, were produced from wrought iron, including rivets, nails, wire, chains, rails, railway couplings, water and steam pipes, nuts, bolts, horseshoes, handrails, wagon tires, straps for timber roof trusses, and ornamental ironwork, among many other things.^{[5][note 1]}

Wrought iron is no longer produced on a commercial scale. Many products described as wrought iron, such as guard rails, garden furniture,^[6] and gates are made of mild steel.^[7] They are described as "wrought iron" only because they have been made to resemble objects which in the past were wrought (worked) by hand by a blacksmith (although many decorative iron objects, including fences and gates, were often cast rather than wrought).^[7]